EP performances Wear scar, DIN 51350/5, 1 400 N, mm | 1.2* |
Lubrication ability R2F, running test B at 120 °C | Pass at 140 °C |
Corrosion protectio Emcor: – standard ISO 11007 | 0–0 |
Water resistance Water wash out ASTM D1264, % | 2 max. |
Water resistance DIN 51 807/1, 3 hrs at 90 °C | 1 max. |
Penetration DIN ISO 2137 60 strokes, 10–1 mm | 265-295 |
EP performances Weld load, DIN 51350/4, N | 4 000* |
ase oil viscosity 40 °C, mm²/s | 450 |
ase oil viscosity 100 °C, mm²/s | 31 |
Copper corrosio DIN 51 811, 100 °C | 1b max. |
NLGI consistency class | 2 |
Operating temperature range | –20 to +140 °C (–4 to +284 °F) |
Dropping point, DIN ISO 2176 | >280 °C (>536 °F) |
Typical applications | Roll stands in metallurgical industry; Continuous casters; Vibrating screens; Ball mills bearings; |
Features & benefits | Good mechanical stability; Excellent corrosion protection; Excellent high load lubricating capacity; Roll stands in metallurgical industry; Continuous casters; Vibrating screens; Ball mills bearings; |
ase oil type | Mineral |
180 kg drum | LGHC 2/180 |
Shelf life | 5 years |
Designatio | LGHC 2/(pack size) |
50 kg drum | LGHC 2/50 |
Soap type | Calcium sulphonate complex |
Pack size | Designation |
Colou | Brown |
DIN 51825 | KP2N-20 |
Penetration DIN ISO 2137 100 000 strokes, 10–1 mm | +30 max. |
Oil separatio DIN 51 817, 7 days at 40 °C, static, % | 2* |
Corrosion protectio Emcor: – salt water test (100% sea water) | 0–1 |
Mechanical stability Roll stability, 50 hrs at 80 °C, 10–1 mm | –20 to +30 max. |