| Copper corrosio DIN 51 811, 120 °C |
1 max. |
| ase oil viscosity 40 °C, mm2/s |
400 |
| – salt water test (1% NaCl) |
0–0 |
| Operating temperature range |
–20 to +120 °C (–4 to +248 °F) |
| Emco – standard ISO 11007 |
0–0 |
| Dropping point DIN ISO 2176 |
170 °C min. (338 °F min) |
| 100 000 strokes, 10–1 mm |
+50 max. |
| – water washout test |
0–0 |
| NLGI consistency class |
1 |
| Typical applications |
Wind turbine main shaft bearings; Large bearing applications; Heavy industrial applications; Centralized lubrication systems; |
| Features & benefits |
Excellent mechanical stability; Very good protection against fretting and wear; Good flow at low starting temperature; Good flow properties that enable easy replenishment within the bearing design; |
| DIN 51825 code |
KP1K-20 |
| 100 °C, mm2/s |
25 |
| ase oil type |
Mineral |
| Designatio |
LGEP 1/(pack size) |
| 18 kg pail |
LGEP 1/18 |
| Thickene |
Lithium-Calcium |
| Colou |
Beige |
| Packsize |
Designation |
| 4-ball test, welding load DIN 51350/4. N |
3400 min. |
| Penetration DIN ISO 2137 60 strokes, 10–1 mm |
310–340 |
| Water resistance DIN 51 807/1, 3 hrs at 90 °C |
1 max. |
| EP performance Wear scar DIN 51350/5, 1 400 N, mm |
1.8 max. |
| Lubrication ability R2F, running test B at 120 °C |
Pass at 80 °C |
| Oil separatio DIN 51 817, 7 days at 40 °C, static, % |
1–5 |
| Mechanical stability Roll stability, 50 hrs at 80 °C, 10–1 mm |
+50 max. |
| Rolling bearing grease life R0F test L50 life at 10 000 r/min., hrs |
1 000 min. at 100 °C |